recommended footprint given on the datasheet. It
is recommended the customer follow this
footprint to assure best assembly and ultimately
reliability performance, as well as from a thermal
performance.
Figure 2: Solder wetted to lead-frame copper
exposed by singulation on lead ends.
PAD FINISH
The most frequently encountered pad finish for
consumer electronics with tin lead solders was hot
air solder leveled, HASL. With lead free, other
finishes are preferred. Immersion silver,
immersion nickel gold and organic surface
protectant, OSP are the board finishes of choice.
Each finish has useful properties, and each has its
challenges. It is beyond the scope of this paper to
debate each system’s merits. Not any one finish
will be right for all applications, but currently the
most commonly seen in large scale consumer
electronics is OSP. A high quality OSP like
Enthone® Entek® Plus HT is recommended.
PWB MATERIAL
It is recommended that lead free FR-4 is used in
PWB construction. Lower quality FR-4 can cause
numerous problems with the reflow temperatures
seen when using lead free solder. IPC-4101B
“Specification for Base Materials for Rigid and
Multilayer Printed Boards” contains further
information on choosing the correct PWB material
for the intended application.
USING VIAS WITH 6x6 DriverMOS
Often the designer will wish to place vias inside of
the center pads. While this is acceptable, the user
should realize that vias often create voiding, and
carefully study the process design with x-ray
inspection of voiding to assure the design is
yielding the expected performance. There are
several types of via. Blind vias are not
recommended due to the fact they often trap gases
generated during reflow and yield high percentages
of voiding. Solder mask can also be placed over
the top of the via to prevent solder from wicking
down the via. It has been shown in previous
studies that this will also create a higher incidence
of voiding than an open through-hole or filled via.
If through hole vias are used, a drill size of 0.3mm
with 1 ounce copper plating yields good
performance. The test board used 4 vias with
favorable results. With through-hole vias, solder
wicking through the hole, or solder protrusion,
must be considered. Opening the solder mask just
enough to keep from plugging the via is
recommended. By not creating a pad for solder to
wet to on the reverse side of the via will help
prevent protrusion. In high reliability applications,
filled vias are the preferred due to lower incidences
of voiding during reflow and eliminating the stress
riser created by a void at the edges of the via barrel.
Figure 3: PWB pad showing OSP pad finish.
STENCIL DESIGN
It is estimated that 60% of all assembly errors are
due to paste printing. For a robust manufacturing
process, it is therefore the most critical phase of